        Coating Resistant Refractory Castable

        Coating Resistant Refractory Castable

        It is made of aluminum silicate material and silicon carbide material as the main materials added with additive.

        REQUEST A QUOTE

        product details

        It is made of aluminum silicate material and silicon carbide material as the main materials added with additive.

         

        Classification:

        It can be divided into four types based on different percentage of SiC, KJP-25, KJP-35, KJP-45, KJP-55, KJP-65.

         

        Application:

        It is used for decomposition furnace slope of NSP kiln, uptake shaft, preheater cone, decomposition furnace lining, industrial furnace lining and other skinning parts. The definite using part should refer to the design of cement design institute. Normally, it is used for decomposition slope.

         

        Item KJP-25 KJP-35 KJP-45 KJP-55
        Max. Service Temp., ℃ 1300 1400 1400 1400
        SiC, %, ≥ 25 35 45 55
        Cold Bending Strength, MPa, ≥ Firing at 1100 ℃ x3h 6 7 8 10
        Cold Crushing Strength, MPa Drying at 110 ℃ x24h 55 60 65 70
        Firing at 1100 ℃ x3h 55 60 65 70
        High Temp. Bending Strength, MPa, ≥ 1100 ℃ 7 7 8 8
        Permanent Linear Change after Reheating, % Firing at 1100 ℃ x3h -0.4~+0.4 -0.4~+0.4 -0.3~+0.3 -0.3~+0.3
        Coating Resistance Level Firing at 1100 ℃ x3h Level 3 Level 2 Level 2 Level 1
        Alkali Resistance Firing at 1100 ℃ x5h Level 2 Level 2 Level 1 Level 1

         

        Coating Resistant Refractory Castable
         

        REQUEST A QUOTE